Title: Green bio-based CaO from guinea fowl eggshells
Authors: Pedavoah, Mary-Magdalene
Badu, Mercy
Boadi, Nathaniel Owusu
Awudza, Johannes A. M.
Keywords: Sustainable Materials
CaO
Biowaste
TGA
SEM-EDX
XRD
Issue Date: 31-May-2018
Publisher: Scientific Research Publishing
Citation: Pedavoah, M.-M., Badu, M., Boadi, N.O. and Awudza, J.A.M. (2018) Green Bio-Based CaO from Guinea Fowl Eggshells. Green and Sustainable Chemistry, 8, 208-219. https://doi.org/10.4236/gsc.2018.82015
Abstract: Eggshells are among the emerging hazardous waste from the food processing industry. This work sought to valorize waste guinea fowl eggshells. Guinea fowl eggshells (GFEs) were evaluated in the production of CaO for chemical and industrial application. The functionality, thermal stability, elemental composition, phase distribution and surface morphology properties of uncalcined GFEs and GFEs calcined at 700˚C, 800˚C, 900˚C, 1000˚C and 1100˚C were systematically studied by FTIR, TGA, XRF, XRD and SEM-EDX respectively. The elemental analysis revealed Ca as the main element in the GFEs. The uncalcined GFEs showed intense peaks that corresponded to calcite (CaCO3) phases. These transformed into Ca(OH)2 as the temperature of calcination increased and finally to CaO in the FTIR analysis. In the XRD diffractograms, the main peaks at 2θ values were 29.466˚ for the uncalcined GFESs and at 37.377˚ for the sample treated at 1100˚C. The phases were confirmed as CaO when compared with JCPDS files. Using the Scherer equation, the CaO crystallite size for the sample calcined at 1100˚C was found to be 50.68 nm along the (2 0 0) orientation. All the samples showed multi-step decomposition patterns in the thermogravimetric analyses (TGA), with weight loss of up to 47% for the uncalcined GFEs sample, which was mainly due to the transformation of the calcite (CaCO3) phase to CaO by removal of bound water, organic components, and CO2. Samples calcined at 1100˚C showed mainly CaO phases in XRD analyses and fairly stable with 7% loss in weight after treatment at 800˚C. SEM images of samples calcined at 900˚C were irregular compared to samples treated at 1100˚C. EDX data revealed that the surface structure was 100% calcium and oxygen. GFEs are a potential source of pure calcium oxide for various industrial uses.
Description: An article published by Scientific Research Publishing and also available at DOI: 10.4236/gsc.2018.82015
URI: http://hdl.handle.net/123456789/12599
Appears in Collections:College of Science

Files in This Item:

File Description SizeFormat
GSC_2018053015101686.pdf1.46 MBAdobe PDFView/Open

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

 

Valid XHTML 1.0! DSpace Software Copyright © 2002-2010  Duraspace - Feedback